LPG sensing characteristics of electrospray deposited SnO2 nanoparticles


Gürbüz M., Günkaya G., Doʇan A.

Applied Surface Science, cilt.318, ss.334-340, 2014 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Özet
  • Cilt numarası: 318
  • Basım Tarihi: 2014
  • Doi Numarası: 10.1016/j.apsusc.2014.09.185
  • Dergi Adı: Applied Surface Science
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.334-340
  • Anahtar Kelimeler: sensor, SnO2 film, Electrospray deposition, Characterization, ZINC-OXIDE FILMS, THIN-FILM, CERAMIC SUSPENSIONS, SPRAY DEPOSITION, TIN-OXIDE, GAS, TEMPERATURE, SENSITIVITY, FABRICATION
  • Anadolu Üniversitesi Adresli: Evet

Özet

© 2014 Elsevier B.V. All rights reserved. In this study, SnO 2 films were fabricated on conductive substrate such as aluminum and platinum coated alumina using electro-spray deposition (ESD) method for gas sensor applications. Solution flow rate, coating time, substrate-nozzle distance and solid/alcohol ratio were studied to optimize SnO 2 film structure. The morphology of the deposited films was characterized by stereo and scanning electron microscopy (SEM). The gas sensing properties of tin oxide films were investigated using liquid petroleum gas (LPG) for various lower explosive limit (LEL). The results obtained from microscopic analyses show that optimum SnO 2 films were evaluated at flow rate of 0.05 ml/min, at distance of 6 cm, for 10 min deposition time, for 20 gSnO 2 /L ethanol ratio and at 7 kV DC electric field. By the results obtained from the gas sensing behavior, the sensitivity of the films was increased with operating temperature. The films showed better sensitivity for 20 LEL LPG concentration at 450 °C operating temperature.