Effect of alkaline earth oxides on the firing behavior of porcelain stonewares Effetto degli ossidi alcalino terrosi sul comportamento in cottura del gres porcellanato

Çigdemir G., Kara A., Kara F.

C e Ca, cilt.40, sa.3, ss.195-204, 2010 (Scopus) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 40 Sayı: 3
  • Basım Tarihi: 2010
  • Dergi Adı: C e Ca
  • Derginin Tarandığı İndeksler: Scopus
  • Sayfa Sayıları: ss.195-204
  • Anadolu Üniversitesi Adresli: Hayır

Özet

Aim of this study was to investigate the relations between chemical composition and firing behaviour of porcelain stoneware formulations. The effects of magnesia and/or calcia incorporation in varying amounts into a standard stoneware formulations through combined use of calcite and magnesite on firing behaviour was studied by means of a non-contact optical dilatometer. It was shown that suitable combination of magnesite/calcite noticeably lowered peak firing temperature without narrowing the firing range. Peak firing temperatures of these bodies were also at commercially acceptable levels. Further formulations prepared with calcite, kaolin and a local clay high in iron oxide content were also shown to give acceptable chromatic co-ordinates. It was also possible to develop bodies with high whiteness values without employing zircon.